自动焊锡机烙铁头主要用途是焊接元器件及导线,因机械结构、功能、用途也有不同的分类。烙铁头是电子部件制作和电器维修的必备工具,使用自动焊锡机进行焊接时,常常会遇到这样的问题,烙铁头不上锡,对于这种情况的出现,导致此情况的原因除了烙铁头本身的问题之外,还可能有其它方面的原因,下面焊锡机厂家帮你分析一下烙铁头不上锡的原因。
The soldering iron head of automatic soldering machine is mainly used for welding components and conductors. There are different classifications for mechanical structure, function and usage. A soldering iron head is a necessary tool for the manufacture of electronic components and electrical maintenance. When using an automatic soldering machine for welding, it is often met with such a problem that the iron head is not SN. For this case, the cause of this situation can be caused by other reasons besides the problem of the iron head itself. The manufacturer will help you analyze the reason why the solder doesn't go to the tin.

焊锡机烙铁头

自动焊锡机烙铁头不上锡的原因分析:
The reason why the soldering iron head of automatic solder machine does not go to tin is analyzed.

1、开机使用前未将烙铁头上锡面上锡,焊接时选择温度过高,容易使烙铁头上锡面与空气中氧气接触发生剧烈氧化,使用的锡丝品质不合格或焊丝中助焊剂中断,使用不正确或是有不恰当的清理方式。
1, the tin surface of the iron head is not on the iron head before the machine is used, and the temperature is too high when welding. It is easy to oxidize the tin surface on the iron head with the oxygen in the air. The quality of the tin wire is not qualified or the flux in the welding wire is interrupted, and the use is incorrect or the improper cleaning method is used.

2、当焊接实时温度超过350℃,而且停止焊接超过1小时,烙铁头上锡量过少,使用的助焊剂是高腐蚀性的,从而引起烙铁头快速氧化,接触到有机化合物如塑料、润滑油或其它化合物。
2. When the welding real-time temperature is over 350, and the soldering over more than 1 hours, the amount of tin on the iron head is too low. The flux used is highly corrosive, which causes the rapid oxidation of the iron head and contact with the organic compounds such as plastic, lubricating oil or other compounds.

3、“干烧”烙铁头,如:智能温度控制器常开不使用,而烙铁头表面无上锡,会引起烙铁头快速氧化,使用中性活性的助焊剂,没有及时的清理烙铁头上的氧化物。
3, "dry burning" iron head, such as: intelligent temperature controller often open not to use, and the iron head surface of no tin, will cause rapid oxidation of the iron head, the use of neutral active flux, no timely cleaning of the oxide on the iron head.

以上就是关于自动焊锡机烙铁头不上锡的原因作出的几点分析,更多关于焊锡机的小知识请关注焊锡机厂家创盈时代,我们是一家专注于双Y双头焊锡机、双头三头焊锡机、三轴四轴焊锡机、激光焊锡设备整体解决方案的高新技术企业。