焊锡机烙铁头不上锡的应对措施

发布时间:2018-04-21 10:21:21   来源:本文搜集于网络,由焊锡机厂家创盈时代整理并发布,转载请注明出处    点击:

焊锡机烙铁头不上锡的应对措施

1、焊接选择温度过高,烙铁头表面附着的锡快速溶解挥发,产生剧烈氧化,高温时要求增加锡量,使用不正确或是有不恰当的清洁方式。建议使用专用的高温清洁海绵,和设备专用烙铁头清洁器。
1,the welding temperature is too high, the tin surface attached to the soldering head quickly dissolves and volatiles, resulting in severe oxidation。 High temperature requires increasing tin content, incorrect or improper cleaning。 It is recommended to use special high temperature cleaning sponge and special iron head cleaner for equipment。

焊锡机烙铁头

2、使用的锡丝纯度不高或锡丝中助焊剂中断。所以企业在采购的时候要确保锡丝质量可靠。当焊接实时温度超过350℃,而且停止焊接超过1小时,烙铁头上锡量过少。 建议设备停机时对烙铁头进行加锡予以保护。
2,the purity of tin wire is not high or the flux of tin wire is interrupted. So when purchasing, ensure that the quality of tin wire is reliable. When the welding temperature is over 350 C and the welding time is more than 1 hours, the tin content on the soldering head is too small. It is recommended that the tin head be protected when the equipment is shut down.

3、干烧烙铁头,智能温度控制器常开不使用,而烙铁头表面没有上锡,会引起烙铁头长期接触空气的氧气快速氧化速度,自动焊锡机使用的助焊剂是高腐蚀性的,从而引起烙铁头快速氧化。选好品质可靠的助焊剂也是保证烙铁头不被快速氧化的原因。
3,dry burning iron head, the intelligent temperature controller often does not use, and the soldering iron head surface does not have tin, will cause the iron head to contact the air fast oxidation speed, the use of welding flux is high corrosion, thus causing rapid oxidation of the iron head. Selecting a reliable flux is also the reason why the iron head is not rapidly oxidized.

4、建议使用中性活性的助焊剂,日常没有及时清理烙铁头上的氧化物,需对烙铁头反复加锡清洗,烙铁头大多是铜做的,铜在高温下会和空气中的氧气反应生成黑色的氧化铜,而氧化铜是不沾锡的。
4,it is suggested that the neutral active flux is used, and the oxide on the iron head is not cleaned in time. It is necessary to clean the iron head repeatedly with tin, and the iron head is mostly made of copper. The copper will react with the oxygen in the air to produce black copper oxide at high temperature, and the copper oxide is not tin.

友情提示:处理烙铁头烧死的方法是将烙铁通电加热至正常温度,然后用锉刀或者砂纸轻微将烙铁头表面的黑色氧化铜打磨掉,之后立即蘸上松香,随后就可以挂上锡。
Friendship tip: the way to deal with the burning of the iron head is to heat the iron to the normal temperature, and then use the file or sand paper to mildly wear the black copper oxide on the surface of the iron head, then dipped in the rosin immediately, and then hang the tin.

更多关于焊锡机的小知识请关注焊锡机厂家创盈时代,我们是一家专注于双Y双头焊锡机、双头三头焊锡机、三轴四轴焊锡机、激光焊锡设备整体解决方案的高新技术企业。

原文地址:http://www.bananacanon.com/news/hxjs/1724.html

本文关键字:焊锡机 烙铁头不上锡