如何避免DIP后焊制程中的锡珠飞溅现象

发布时间:2019-08-12 15:29:48   来源:本文搜集于网络,由深圳焊锡机厂家创盈时代整理并发布,欢迎转载    点击:

DIP后焊制程大致可分为手工焊接,自动送锡焊台焊接,自动焊锡机焊接三种类型。后焊制程中经常会遇到过锡珠飞溅这种现象,那么我们在操作过程中如何避免DIP后焊制程中的锡珠飞溅现象呢?
DIP post-welding process can be broadly divided into manual welding, automatic solder ingress welding, automatic solder ingress machine welding three types。 After welding process often encountered the phenomenon of tin beads splashing, then how do we in the operation process to avoid the phenomenon of tin beads splashing in the DIP post-welding process?

手工焊接前采用自动破锡机提前对焊锡丝进行破锡处理后再使用,其原理就是在破锡机自动送出锡线时利用经过特殊设计的圆形破锡刀片在锡线上打出一个个小孔,这样在焊接时就会使里面的助焊剂在烙铁加热时气化,在锡线融化之前渗出一部分,从而达到降低锡珠飞溅的目的。
Hand welding before the use of automatic tin-breaking machine in advance of the solder wire for tin treatment and then use, the principle is that when the tin-breaker automatically sends the tin line, the use of specially designed circular tin-breaking blade sin-breaking blade in the tin line to make a small hole, so that in welding will make the inside of the flux gasification when the iron is heated, before the tin wire melts out of a part, This is to reduce the splash of tin beads.

焊锡机

使用自动焊锡机降低锡珠飞溅,在送锡过程中给锡丝进行100°C左右的预热处理、再送到烙铁头最前端焊接产品、可以减少焊锡丝焊接时温度的急剧变化,从而达到降低锡珠飞溅的目的,此外由于锡丝预热装置体积相对偏大,在设备的现场使用过程中具有一定的局限性,因此在自动焊锡机上使用此种送锡方式的较少。
The use of automatic solder machine to reduce tin beads splash, in the delivery of tin to the tin wire about 100 degrees C warm-up treatment, and then sent to the soldering head of the front welding products, can reduce the rapid change in the temperature of solder wire welding, so as to achieve the purpose of reducing the tin bead splash, in addition to the tin wire preheating device relatively large, There are some limitations in the field use of equipment, so this kind of tin delivery method is used less on automatic solder ingenuity machine.   

破锡型精密送锡系统,在自动送锡的同时、利用经过特殊设计的圆形破锡刀片在锡线上打出一个个小孔,这样就会使里面的助焊剂在烙铁加热时气化,在锡线融化之前渗出一部分,从而达到降低锡珠飞溅的目的,此种方法是目前市场上应用最为广泛的主流技术。
Breaking tin-type precision delivery system, in the automatic delivery of tin at the same time, the use of specially designed circular tin blade in the tin line to make a small hole, so that the inside of the flux in the iron heating gasification, before the tin line melts out part, so as to achieve the purpose of reducing the tin beads splashing, This approach is the most widely used mainstream technology on the market today。

更多关于焊锡机的小知识请关注焊锡机厂家创盈时代,我们是一家专注于双Y双头焊锡机、双头三头焊锡机、三轴四轴焊锡机、激光焊锡设备整体解决方案的高新技术企业。

原文地址:http://www.bananacanon.com/news/hxjs/1806.html